Zamak de lingote de liga de zinco (3 # 5 # 8 #)

\ n Lingote de liga de zinco Zamak # 3 # 5 # 8 \ n Al%: 3.8-4.2% \ n \ n Zamak 5 propriedadesPropertyMetric valueEnglish valuePropriedades mecânicasPropriedades físicas \ n

Ultimate tensile strength	331 MPa (270 MPa aged)	48,000 psi (39,000 psi aged)
Yield strength (0.2% offset)	295 MPa	43,000 psi
Impact strength	52 J (56 J aged)	38 ft-lbf (41 ft-lbf aged)
Elongation at Fmax	2%
Elongation at fracture	3.6% (13% aged)
Shear strength	262 MPa	38,000 psi
Compressive yield strength	600 MPa	87,000 psi
Fatigue strength (reverse bending 5x108cycles)	57 MPa	8,300 psi
Hardness	114 Brinell
Modulus of elasticity	96 GPa	14,000,000 psi
Solidification range (melting range)	380386 °C	716727 °F
Density	6.7 kg/dm3	0.24 lb/in3
Coefficient of thermal expansion	27.4 μm/m-°C	15.2 μin/in-°F
Thermal conductivity	109 W/mK	756 BTU-in/hr-ft2-°F
Electrical resistivity	6.54 μΩ-cm at 20 °C	2.57 μΩ-in at 68 °F
Latent heat (heat of fusion)	110 J/g	4.7x10-5 BTU/lb
Specific heat capacity	419 J/kg-°C	0.100 BTU/lb-°F
Coefficient of friction	0.08

\ n USAGE: \ n \ n \ n 1. Usado principalmente para a indústria de baterias de liga de fundição \ n \ n 2. Amplamente utilizado na indústria de pintura / impressão / tinturaria / farmacêutica / borracha, etc. \ n \ n 3. Indústrias químicas , zinco e outra indústria de revestimentos de chapeamento de ligas metálicas \ n \ n 4. Em zincagem, fabricação de latão, bronze de maganese, ferro galvanizado, bateria seca; como catalisador e agente redutor. \ n \ n \ n \ n

Grupo de Produto : Material de metal